Oval Clip-It Core (0361184751)
61 OVAL CABLE CORE ASSEMBLY
61 Material
Suppression Components
Cable Component
Printer Friendly Data Sheet
Check Stock

Part Number: 0361184751
61 OVAL CABLE CORE ASSEMBLY
Explanation of Part Numbers:
– Digits 1 & 2 = Product Class
– Digits 3 & 4 = Material Grade
The B dimension is the core inside diameter.
Weight: 65 (g)
Dim | mm | mm tol | nominal inch | inch misc. |
A | 30.43 | +/- 1.0 | 1.20 | _ |
B | 19.20 | _ | 0.75 min | |
C | 29.90 | +/- 1.0 | 1.18 | _ |
D | 23.0 | +/- 1.0 | 0.91 | _ |
E | 9.2 | _ | 0.36 min |
Chart Legend
+ Test frequency
•For solid cable cores, see Round Cable EMI Suppression Cores
Typical Impedance (Ω) | |
100 MHz+ | 139 |
250 MHz | 232 |
Electrical Properties | |
Ae(cm2) | 1.27 |
Σl/A(cm-1) | 0.583 |
le(cm) | .741 |
Ve(cm3) | 94.10 |
Round cable snap-it assemblies are controlled for impedances only. Minimum impedance values are specified for the + marked frequencies. The minimum impedance is typically the listed impedance less 20%.
Single turn impedance tests for 31, 43 and 46 material cores are performed on the E4991A/HP4291B Impedance Analyzer. The 61 material parts are tested on the E4991A / HP4291B Impedance Analyzer and 75 material parts are tested on the E4990A Impedance Analyzer. Cores are tested with the shortest practical wire length.
Typical Impendance (Ω) | |
100 MHz+ | 139 |
250 MHz | 232 |
A high frequency NiZn ferrite developed for a range of inductive applications up to 25 MHz. This material is also used in EMI applications for suppression of noise frequencies above 200 MHz. Excellent stability characteristics.
Strong magnetic fields or excessive mechanical stresses may result in irreversible changes in permeability and losses.
Available in 61 material™:
EMI Suppression Beads
Beads On Leads
SM beads
Wound Beads
Multi-Aperture Cores
Round Cable Snap-Its
Toroids
Rods
Antenna/RFID
Rods
Round EMI Suppression Cores
61 Material™ Characteristics
Property | Unit | Symbol | Value |
Initial Permeability @ B < 10 gauss | µi | 125 | |
Flux Density @ Field Strength | Gauss Oersted |
B H |
2500 15 |
Residual Flux Density | Gauss | Br | 1000 |
Coercive Force | Oersted | Hc | 1.2 |
Loss Factor @ Frequency | 10 -6 MHz |
Tan δ/ µi | 90 10 |
Temperature Coefficient of Initial Permeability (20 -70°C) | %/°C | .10 | |
Curie Temperature | °C | Tc | >300 |
Resistivity | ohm-cm | ρ | 1×108 |
**** Characteristic curves are measured on standard Toroids (18/10/6 mm) at 25°C and 10 kHz unless otherwise indicated. Impedance characteristics are measured on standard shield beads (3.5/1.3/6.0 mm) unless otherwise indicated.
Material Safety Data Sheet (MSDS)
Click here to download Complex Permeability vs. Frequency (CSV)
Click here to download 61 Material Power Loss Density vs. Flux Density at 25°C
Ferrite Material Constants
Storage and Operating Temperature
Printer Friendly Data Sheet - Download as pdf file