95 Material Data Sheet
A low loss MnZn ferrite material for power applications up to 200 kHz with low temperature variation. New type of 95 material is a low loss power material which features less power loss variation over temperature (25-100°C) at moderate flux densities for operation below 200 kHz.
Available in 95 material:
Pot Cores
RM
PQ
EFD
EP
95 Material Characteristics
| Property | Unit | Symbol | Value |
| Initial Permeability @ B < 10 gauss | µi | 3000 | |
| Flux Density @ Field Strength | Gauss Oersted |
B H |
5000 5 |
| Residual Flux Density | Gauss | Br | 1200 |
| Coercive Force | Oersted | Hc | 0.18 |
| Loss Factor @ Frequency | 10 -6 MHz |
Tan δ/ µi | 2.5 0.1 |
| Temperature Coefficient of Initial Permeability (20 -70°C) | %/°C | 0.6 | |
| Curie Temperature | °C | Tc | >220 |
| Resistivity | Ohm-cm | ρ | 200 |
**** Characteristic curves are measured on standard Toroids (18/10/6 mm) at 25°C and 10 kHz unless otherwise indicated. Impedance characteristics are measured on standard shield beads (3.5/1.3/6.0 mm) unless otherwise indicated.